Full metadata record
DC poleHodnotaJazyk
dc.contributor.authorMálek, Jaroslav
dc.contributor.authorHnilica, František
dc.contributor.authorVeselý, Jaroslav
dc.contributor.authorSmola, Bohumil
dc.contributor.authorMedlín, Rostislav
dc.date.accessioned2018-02-21T11:35:25Z-
dc.date.available2018-02-21T11:35:25Z-
dc.date.issued2017
dc.identifier.citationMÁLEK, J., HNILICA, F., VESELÝ, J., SMOLA, B., MEDLÍN, R. The effect of annealing temperature on the properties of powder metallurgy processed TI-35NB-2ZR-0.5O alloy. Journal of the Mechanical Behavior of Biomedical Materials, 2017, roč. 75, č. November 2017, s. 252-261. ISSN 1751-6161.en
dc.identifier.issn1751-6161
dc.identifier.urihttp://hdl.handle.net/11025/29269
dc.description.abstractSlitina Ti-35Nb-2Zr-0,5O (hmotnostní %) byla vyrobena procesem práškové metalurgie (izostatické lisování za studena směsi elementárních prášků a následné slinování) s primárním cílem použití jako materiálu pro biologické aplikace. Sintrované vzorky byly promyty a následně byl zkoumán vliv teploty žíhání na mechanické a strukturní vlastnosti. Vzorky byly žíhány při teplotě 800, 850, 900, 950 a 1000 ° C po dobu 0,5 hodiny s kalením do vody. Byly pozorovány významné změny v mikrostruktuře (tj. Rozpouštění sraženiny nebo zrychlení zrna) ve vztahu ke zvýšení teploty žíhání. Ve spojení s těmito změnami byly také zkoumány mechanické vlastnosti. Konečná pevnost v tahu se zvýšila z 925 MPa (vzorek žíhaný při 800 ° C) na 990 MPa (900 ° C). Také prodloužení (plasticita) narostla z ~ 13% (800 ° C) na více než 20% (900, 950 a 1000 ° C).cs
dc.format10 s.cs
dc.format.mimetypeapplication/pdf
dc.language.isoenen
dc.publisherElsevieren
dc.rightsPlný text není přístupný.cs
dc.rights© Elsevieren
dc.subjectSlitiny beta-titanu, žíhání, mechanické vlastnosti, plasticita, fraktografie.cs
dc.titleEfekt teploty žíhání na vlastnosti metalurgicky zpracované práškové slitiny Ti-35Nb-2Zr-0.5O.cs
dc.titleThe effect of annealing temperature on the properties of powder metallurgy processed TI-35NB-2ZR-0.5O ALLOYen
dc.typečlánekcs
dc.typearticleen
dc.rights.accessclosedAccessen
dc.type.versionpublishedVersionen
dc.description.abstract-translatedTi-35Nb-2Zr-0.5O (wt.%) alloy was prepared via a powder metallurgy process (cold isostatic pressing of blended elemental powders and subsequent sintering) with the primary aim of using it as a material for bio-applications. Sintered specimens were swaged and subsequently the influence of annealing temperature on the mechanical and structural properties was studied. Specimens were annealed at 800, 850, 900, 950, and 1000 °C for 0.5 h and water quenched. Significant changes in microstructure (i.e. precipitate dissolution or grain coarsening) were observed in relation to increasing annealing temperature. In correlation with those changes, the mechanical properties were also studied. The ultimate tensile strength increased from 925 MPa (specimen annealed at 800 °C) to 990 MPa (900 °C). Also the elongation increased from ~13% (800 °C) to more than 20% (900, 950, and 1000 °C).en
dc.subject.translatedbeta-titanium alloys, annealing, mechanical properties, plasticity, fractographyen
dc.identifier.doi10.1016/j.jmbbm.2017.07.032
dc.type.statusPeer-revieweden
dc.identifier.obd43919461
dc.project.IDinfo:eu-repo/grantAgreetment/EC/Výpočetní a experimentální design pokročilých materiálů s novými funkcionalitami /CZ.02.1.01/0.0/0.0/15_003/0000358cs
Vyskytuje se v kolekcích:OpenAire
Články / Articles (CTM)
OBD

Soubory připojené k záznamu:
Soubor VelikostFormát 
Medlin_The effect of annealing.pdf1,41 MBAdobe PDFZobrazit/otevřít  Vyžádat kopii
Zobrazit minimální záznam Zobrazit statistiky


Použijte tento identifikátor k citaci nebo jako odkaz na tento záznam: http://hdl.handle.net/11025/29269

Všechny záznamy v DSpace jsou chráněny autorskými právy, všechna práva vyhrazena.

hledání
navigace
  1. DSpace at University of West Bohemia
  2. Publikační činnost / Publications
  3. OBD