| Název: | Heat treatment with bainitic hold of CMnSiAI steel |
| Autoři: | Jandová, Andrea Kučerová, Ludmila Rubešová, Kateřina |
| Citace zdrojového dokumentu: | JANDOVÁ, A., KUČEROVÁ, L., RUBEŠOVÁ, K. Heat treatment with bainitic hold of CMnSiAI steel. In: Conference Proceedings - METAL 2017 - 26th International Conference on Metallurgy and Materials. Ostrava: TANGER Ltd., 2017. s. 802-806. ISBN 978-80-87294-79-6. |
| Datum vydání: | 2017 |
| Nakladatel: | Tanger |
| Typ dokumentu: | konferenční příspěvek conferenceObject |
| URI: | http://hdl.handle.net/11025/30912 |
| ISBN: | 978-80-87294-79-6 |
| Klíčová slova v dalším jazyce: | TRIP steel;partial substitution;retained austenite |
| Abstrakt v dalším jazyce: | TRIP (transformation induced plasticity) steel are modern structural materials which are currently mainly used in an automotive industry. The processing of these steels utilize an effect of transformation induced plasticity resulting in good mechanical properties - high strength (up to 1200 MPa) and formability (around 35 %). TRIP effect is based on stabilisation of sufficient amount of retained austenite and its transformation into strain induced martensite in consequence of applied plastic deformation at low temperature. The properties of this steel are based on a multiphase microstructure, which consists of ferrite, bainite and retained austenite. In this work, CMnSiAI steel was heat treated using various processing parameters. Three different temperature of austenitization (850 - 900 - 950 degrees C) were applied and the samples were subsequently cooled by cooling rates in the range of 26 - 32 degrees C / s to different bainitic hold temperatures ranging 410 - 460 degrees C. The resulting microstructures were evaluated with use of optical and scanning electron microscopy and volume fraction of retained austenite was determined using X-ray diffraction phase analysis. Mechanical properties of this steel were established by HV10 hardness measurement, which reached the values 260 - 301 HV10. |
| Práva: | Plný text je přístupný v rámci univerzity přihlášeným uživatelům. © Tanger |
| Vyskytuje se v kolekcích: | Konferenční příspěvky / Conference Papers (RTI) OBD |
Soubory připojené k záznamu:
| Soubor | Velikost | Formát | |
|---|---|---|---|
| Heat Treatment with Bainitic Hold of CMnSiAl Steel_pages 802-806.pdf | 2,17 MB | Adobe PDF | Zobrazit/otevřít Vyžádat kopii |
Použijte tento identifikátor k citaci nebo jako odkaz na tento záznam:
http://hdl.handle.net/11025/30912Všechny záznamy v DSpace jsou chráněny autorskými právy, všechna práva vyhrazena.