Title: Influence of chemical composition and parameters of heat treatment on the mechanical properties and microstructure of TRIP steels
Authors: Bublíková, Dagmar
Jirková, Hana
Jeníček, Štepán
Vrtáček, Jiří
Citation: JIRKOVÁ, Hana ed.; JENÍČEK, Štepán ed. Proceedings PING 2019: modern trends in material engineering: 10.-13.09.2019, Pilsen. 1. vyd. Plzeň: University of West Bohemia, 2019, s. 30. ISBN 978-80-261-0879-5.
Issue Date: 2019
Publisher: University of West Bohemia
Document type: konferenční příspěvek
URI: http://hdl.handle.net/11025/35219
ISBN: 978-80-261-0879-5
Keywords: TRIP oceli;zadržený austenit;rentgenová difrakce;mezikritické žíhání
Keywords in different language: TRIP steels;retained austenite;X-ray diffraction;intercritical annealing
Abstract in different language: Good mechanical properties of steels, in which appropriate heat treatment can produce mixed hardening structures, make them candidates for a broad range of applications, namely in the automotive industry. TRIP steels (in which transformation-induced plasticity operates) with a carbon content of approximately 0.2% are one such class of steels. Heat treatment of these steels comprises two stages. The first involve heating to the intercritical region between the A1 and A3. It is followed by cooling to a bainitic transformation temperature and holding. The resulting mixed microstructure consist of ferrite, bainite and retained austenite. Thanks to the presence of ferrite and retained austenite, the ultimate strength and elongation can reach 1500 MPa and 25-40%, respectively. The experiments presented in this paper were performed on two steels whose chemistries were specially adjusted to support formation of TRIP microstructure. The main difference between them was the level of chromium. Intercritical annealing was carried out on both steels. Aspects of interest included mainly the effect of the cooling rate above the bainitic transformation temperature and the holding time on mechanical properties and final microstructure. The heat treatment led to microstructures ferrite, bainite and retained austenite. The strength was under 1100 MPa and elongation reached 28%.
Rights: © University of West Bohemia
Appears in Collections:Proceedings PING 2019: modern trends in material engineering
Konferenční příspěvky / Conference Papers (RTI)
Proceedings PING 2019: modern trends in material engineering

Files in This Item:
File Description SizeFormat 
Bublikova.pdfPlný text180,34 kBAdobe PDFView/Open

Please use this identifier to cite or link to this item: http://hdl.handle.net/11025/35219

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.