| Název: | Influence of higher partitioning temperatures on mechanical properties of heat treated high-strength steel alloyed with 1.3 % chromium |
| Autoři: | Janda, Tomáš Peković, Michal Rubešová, Kateřina Stehlík, Adam |
| Citace zdrojového dokumentu: | JIRKOVÁ, Hana ed.; JENÍČEK, Štepán ed. Proceedings PING 2019: modern trends in material engineering: 10.-13.09.2019, Pilsen. 1. vyd. Plzeň: University of West Bohemia, 2019, s. 34. ISBN 978-80-261-0879-5. |
| Datum vydání: | 2019 |
| Nakladatel: | University of West Bohemia |
| Typ dokumentu: | konferenční příspěvek conferenceObject |
| URI: | http://hdl.handle.net/11025/35223 |
| ISBN: | 978-80-261-0879-5 |
| Klíčová slova: | QP proces;vysokopevnostní ocel;zadržený austenit;mechanické vlastnosti;mikrostruktura |
| Klíčová slova v dalším jazyce: | QP process;high strength steel;retained austenite;mechanical properties;microstructure |
| Abstrakt v dalším jazyce: | This paper deals with the innovative Quenching and partitioning (QP) heat treatment (HT) of low-alloyed chromium steel, and is especially focused on the higher temperatures of partitioning as well as longer holding times and its influence on mechanical properties of the material. As part of the experiment various HT, metallographic analysis, hardness measurement, X-ray diffraction phase analysis (to determine retained austenite content), tensile test and Charpy impact test were performed. In QP treated specimens the best combination of UTS and elongation was observed after quenching in 200 °C salt bath and partitioning at 250 °C for 30 minutes. This specimen showed the UTS above 1900 MPa, elongation of 14 % and also good impact toughness (34 J). Equally good values of impact toughness (36 J) were also observed in the specimens partitioned at 300 °C or 320 °C for holding times up to 30 minutes. On the other side longer partitioning times at the temperature of 320 °C affected the elongation and impact toughness negatively. |
| Práva: | © University of West Bohemia |
| Vyskytuje se v kolekcích: | Proceedings PING 2019: modern trends in material engineering Konferenční příspěvky / Conference Papers (RTI) Proceedings PING 2019: modern trends in material engineering |
Soubory připojené k záznamu:
| Soubor | Popis | Velikost | Formát | |
|---|---|---|---|---|
| Janda.pdf | Plný text | 180,11 kB | Adobe PDF | Zobrazit/otevřít |
Použijte tento identifikátor k citaci nebo jako odkaz na tento záznam:
http://hdl.handle.net/11025/35223Všechny záznamy v DSpace jsou chráněny autorskými právy, všechna práva vyhrazena.