Název: Intermetallics formation during hot dip galvanizing of high carbon steel
Autoři: Gogola, Peter
Gabalcová, Zuzana
Suchánek, Henrik
Kusý, Martin
Citace zdrojového dokumentu: JIRKOVÁ, Hana ed.; JENÍČEK, Štepán ed. Proceedings PING 2019: modern trends in material engineering: 10.-13.09.2019, Pilsen. 1. vyd. Plzeň: University of West Bohemia, 2019, s. 124. ISBN 978-80-261-0879-5.
Datum vydání: 2019
Nakladatel: University of West Bohemia
Typ dokumentu: konferenční příspěvek
conferenceObject
URI: http://hdl.handle.net/11025/35278
ISBN: 978-80-261-0879-5
Klíčová slova: zinek;železo;intermetalické fáze;vysoce uhlíková ocel
Klíčová slova v dalším jazyce: zinc;iron;intermetallic phases;high-carbon steel
Abstrakt v dalším jazyce: From the moment of immersion, the reaction between molten zinc and solid steel starts forming intermetallic phases. This diffusion-controlled process is largely responsible for the final phase composition of zinc coatings. Several literature sources describe this phenomenon for interstitial free steels, but high-carbon steels are rarely being used as substrates. Therefore, in this work high-carbon steel substrates were used. Multiple samples were created by hot-dipping at various immersion temperatures ranging from 450 to 490 °C and times from 24 to 60 s to investigate mainly the morphology of the obtained intermetallic phase layers. Investigation was carried out mainly by SEM on 20 condition, where several hundred sites were investigated in total to achieve statistically relevant information. It was found that while increasing the immersion time influences mainly the thickness of individual intermetallic phase layers, the temperature influenced mainly their morphology. It was also observed that these results are significantly different compared to ones found in literature for interstitial free steels.
Práva: © University of West Bohemia
Vyskytuje se v kolekcích:Proceedings PING 2019: modern trends in material engineering
Proceedings PING 2019: modern trends in material engineering

Soubory připojené k záznamu:
Soubor Popis VelikostFormát 
Gogola.pdfPlný text180,09 kBAdobe PDFZobrazit/otevřít


Použijte tento identifikátor k citaci nebo jako odkaz na tento záznam: http://hdl.handle.net/11025/35278

Všechny záznamy v DSpace jsou chráněny autorskými právy, všechna práva vyhrazena.