Full metadata record
DC poleHodnotaJazyk
dc.contributor.authorBricín, David
dc.contributor.authorAckermann, Michal
dc.contributor.authorJansa, Zdeněk
dc.contributor.authorKubátová, Dana
dc.contributor.authorKříž, Antonín
dc.contributor.authorŠpirit, Zbyněk
dc.contributor.authorŠtafka, Jiří
dc.date.accessioned2021-03-01T11:00:28Z-
dc.date.available2021-03-01T11:00:28Z-
dc.date.issued2020
dc.identifier.citationBRICÍN, D., ACKERMANN, M., JANSA, Z., KUBÁTOVÁ, D., KŘÍŽ, A., ŠPIRIT, Z., ŠTAFKA, J. Development of the structure of cemented carbides during their processing by SLM and HIP. Metals, 2020, roč. 10, č. 11. ISSN 2075-4701.cs
dc.identifier.issn2075-4701
dc.identifier.uri2-s2.0-85095729127
dc.identifier.urihttp://hdl.handle.net/11025/42786
dc.description.abstractPředložená studie se zabývá vývojem struktury práškové směsi WC-Co a to při jejím postupném zpracování SLM a HIP technologií. Použitá prášková směs obsahovala 13±0.6% hmotnostní podíl pojiva Co a WC frakci o průměrné velikosti zrna(3.0±1.9) μm.Jejím zpracováním SLM technologií došlo, v důsledku aplikace různé hustoty energie (VED), k vývoji různého stupně hustoty vytvářených vzorků. Při vysokých hodnotách VED bylo dosaženo hustoty až 88 %. Aplikovaná hodnota VED ovlivnila kromě hustoty pórů, které se ve struktuře vzorků vytvářely, typy strukturních fází a hrubost WC fáze. Při vysokých hodnotách VED se ve struktuře vzorků začaly utvářet trhliny, které vznikaly v důsledku zkřehnutí struktury vzorků a to z několika důvodů, mezi které patřilo hrubnutí α-fáze (WC), vypařování β-fáze (pojiva Co) a precipitace η-fáze. Při nízkých hodnotách VED byla oproti tomu struktura pórů tvořena převážně tvarově nesymetrickými póry, i o velikosti vyšší jak 500 μm. Následným zpracováním vybraných vzorků technologií HIP bylo dosaženo zvýšení jejich hustoty až na hodnotu 96 % kompaktního materiálu. Na tomto zvýšení hustoty se podílely strukturní přeměny zejména pak opětovné hrubnutí α-fáze až o 1300 % oproti původní velikosti zrna práškové směsi a vývoj η-fáze ve struktuře analyzovaných vzorků. Na základě získaných výsledků pak bylo možné rozhodnout o dalším směřování experimentálního programu, který se do větší hloubky bude zabývat zpracováním vybraných práškových směsí WC-Co technologiemi SLM a HIP za doposud nerealizovaných parametrů jejich zpracování.cs
dc.format17 s.cs
dc.format.mimetypeapplication/pdf
dc.language.isoenen
dc.publisherMDPIen
dc.relation.ispartofseriesMetalsen
dc.rights© MDPIen
dc.subjectWC-Cocs
dc.subjectslinuté karbidycs
dc.subjectSLMcs
dc.subjectHIPcs
dc.subjectpórovitostcs
dc.subjecthrubnutí zrnacs
dc.subjectéta fázecs
dc.subjecthustotacs
dc.subjectstruktura SKcs
dc.titleDevelopment of the structure of cemented carbides during their processing by SLM and HIPen
dc.title.alternativeVývoj struktury slinutých karbidů při jejich zpracování procesem SLM a HIPcs
dc.typečlánekcs
dc.typearticleen
dc.rights.accessopenAccessen
dc.type.versionpublishedVersionen
dc.description.abstract-translatedThe study focuses on microstructural evolution in a WC-Co powder mixture during Selective Laser Melting (SLM) and hot isostatic pressing (HIP) processing. This powder mixture contained a 13 plus/minus 0.6 % weight fraction of Co binder and WC particles of mean size of 3.0 plus/minus 1.9 μm. SLM of the mixture produced samples of various densities, depending on the volumetric energy density (VED) applied. High VED levels led to densities of up to 88%. The aspects affected by changes in VED included the pore density as well as the resulting types of phases and the size of WC phase particles. At high VED, the material began to develop cracks due to embrittlement. This had multiple causes: coarsening of a-phase (WC), evaporation of b-phase (Co binder), and precipitation of h-phase. At low VED levels, pores formed, typically of nonsymmetric shapes, with sizes larger than 500 μm. Subsequent HIP processing led to an increased density, up to 96 % of solid material. Contributions to this increased density were provided by structure transformations, namely, coarsening of a-phase by up to 1300 % when compared to the powder grain size, and formation of h-phase. The results provided a basis for steering further research to explore to a greater depth the SLM and HIP processing of selected WC-Co powder mixtures with as yet unused ranges of process parameters.en
dc.subject.translatedWC-Coen
dc.subject.translatedcemented carbidesen
dc.subject.translatedSLMen
dc.subject.translatedHIPen
dc.subject.translatedporosityen
dc.subject.translatedgrain coarseningen
dc.subject.translatedeta phaseen
dc.subject.translateddensityen
dc.subject.translatedCC structuresen
dc.identifier.doi10.3390/met10111477
dc.type.statusPeer-revieweden
dc.identifier.document-number593452500001
dc.identifier.obd43931896
dc.project.IDSGS-2018-051/Aplikace nových postupů úpravy a testování povrchu i objemových materiálů za účelem zvýšení uplatnitelnosti konstrukčního celku nebo pracovního nástroje v průmyslové praxics
dc.project.IDLQ1603/R4S - SUSENcs
dc.project.IDTJ01000218/Výroba prototypového karbidického řezného nástroje aditivní technologií SLMcs
dc.project.IDED2.1.00/03.0108/SUSEN - Udržitelná energetikacs
dc.project.IDEF15_008/0000293/Udržitelná energetika (SUSEN) - 2. fázecs
dc.project.ID90013/Velká výzkumná infrastruktura povinnost (J) - LINDAT/CLARINcs
Vyskytuje se v kolekcích:Konferenční příspěvky / Conference Papers (RTI)
Konferenční příspěvky / Conference papers (KTO)
Konferenční příspěvky / Conference papers (KMM)
OBD

Soubory připojené k záznamu:
Soubor VelikostFormát 
Bricin_Metals_2020.pdf18,93 MBAdobe PDFZobrazit/otevřít


Použijte tento identifikátor k citaci nebo jako odkaz na tento záznam: http://hdl.handle.net/11025/42786

Všechny záznamy v DSpace jsou chráněny autorskými právy, všechna práva vyhrazena.

hledání
navigace
  1. DSpace at University of West Bohemia
  2. Publikační činnost / Publications
  3. OBD