dc.identifier.citationKUČEROVÁ, L., BYSTRIANSKÝ, M., JENÍČEK, Š. Thermo-mechanical Treatment of 0.4C-0.6Mn-2Si Steel with Various Soaking and Annealing Hold Temperatures. Manufacturing Technology, 2019, roč. 19, č. 01_2019, s. 95-100. ISSN 1213-2489.en
dc.identifier.issn1213-2489
dc.identifier.uri2-s2.0-85063354603
dc.identifier.urihttp://hdl.handle.net/11025/34842
dc.description.abstractStředně uhlíková nízko legovaná ocel 0.4C-0.6Mn-2Si byla podrobena tepelně-mechanickému zpra-cování typickému pro TRIP (transformation induced plasticity) ocel. Zpracování bylo tvořeno ohře-vem na teploty 850 -1000 °C a chlazením rychlostí 30 °C/s na různé teploty žíhání v intervalu teplot bainitické transformace 350-500 °C. Během ochlazování byly provedeny dvě tlakové deformace, druhá vždy na teplotě 720 °C. Výsledné mikrostruktury byly analyzovány světlenou a řádkovací elektronovou mikroskopií. RTG difrakční fázová analýza byla použita ke kvantifikaci zbytkového austenitu a mechanické vlastnosti byly stanoveny zkouškou tahem. Mez pevnosti dosahovala hodnot 847-963 MPa a byla doprovázeny vysokou tažností 30-40%. Byly získány vícefázové mikrostruktury tvořené různými podíly feritu, bainitu, zbytkového austenitu a perlitu.cs
dc.format6 s.cs
dc.format.mimetypeapplication/pdf
dc.language.isoenen
dc.publisherUniverzita J. E. Purkyněcs
dc.rightsPlný text je přístupný v rámci univerzity přihlášeným uživatelům.cs
dc.rights© Univerzita J. E. Purkyněen
dc.subjectstředně uhlíková ocelcs
dc.subjecttepelně-mechanické zpracovánícs
dc.subjectzbytkový austenitecs
dc.subjectTRIP ocelcs
dc.titleThermo-mechanical Treatment of 0.4C-0.6Mn-2Si Steel with Various Soaking and Annealing Hold Temperaturesen
dc.title.alternativeTermo-mechanické zpracování oceli 0,4-0,6n-2Si s různými teplotami namáčení a žíhánícs
dc.typečlánekcs
dc.typearticleen
dc.rights.accessrestrictedAccessen
dc.type.versionpublishedVersionen
dc.description.abstract-translatedMiddle carbon low alloyed steel 0.4C-0.6Mn-2Si was subjected to thermo-mechanical treatment typical for TRIP (transformation induced plasticity steels). The processing consisted from soaking at the temperatures of 850-1000 °C and cooling at 30 °C/s to various annealing holds in bainite transformation temperature interval of 350-500 °C. During the cooling from the soaking temperature, two compressive deformations were carried out, the second one always at 720 °C. Resulting microstructures were analysed using light and scanning electron microscopy. X-ray diffraction phase analysis was carried out to establish volume fraction of retained austenite and mechanical properties were measured by tensile test. Tensile strengths in the region of 847-963 MPa were obtained and very good total elongations of 30-40% were achieved at the same time. Multiphase microstructures were obtained with various amounts of ferrite, bainite, retained austenite and pearlite.en
dc.subject.translatedMiddle carbon steelen
dc.subject.translatedThermo-mechanical treatmenten
dc.subject.translatedRetained austeniteen
dc.subject.translatedTRIP steelen
dc.identifier.doi10.21062/ujep/250.2019/a/1213-2489/mt/19/1/95
dc.type.statusPeer-revieweden
dc.identifier.obd43925882
dc.project.IDLO1502/RoRTI - Rozvoj Regionálního technologického institutucs
Vyskytuje se v kolekcích:Články / Articles (RTI)
OBD

Soubory připojené k záznamu:
Soubor VelikostFormát 
Thermo-mechanical Treatment of 0.4C-0.6Mn-2Si Steel with Various Soaking and Annealing Hold Temperatures.pdf1,02 MBAdobe PDFZobrazit/otevřít  Vyžádat kopii
Zobrazit minimální záznam Zobrazit statistiky


Použijte tento identifikátor k citaci nebo jako odkaz na tento záznam: http://hdl.handle.net/11025/34842

Všechny záznamy v DSpace jsou chráněny autorskými právy, všechna práva vyhrazena.

hledání
navigace
  1. DSpace at University of West Bohemia
  2. Publikační činnost / Publications
  3. OBD