Full metadata record
DC poleHodnotaJazyk
dc.contributor.authorJanda, Tomáš-
dc.contributor.authorLeták, Radek-
dc.contributor.authorSkřivanová, Nikola-
dc.contributor.authorVolkmannová, Julie-
dc.contributor.authorJirková, Hana-
dc.contributor.authorKučerová, Ludmila-
dc.date.accessioned2023-01-23T11:00:19Z-
dc.date.available2023-01-23T11:00:19Z-
dc.date.issued2022-
dc.identifier.citationJANDA, T. LETÁK, R. SKŘIVANOVÁ, N. VOLKMANNOVÁ, J. JIRKOVÁ, H. KUČEROVÁ, L. Influence of processing parameters of medium manganese steel with 5% mn on the development of mechanical properties. In Proceedings 31st International Conference on Metallurgy and Materials. Brno: TANGER Ltd., 2022. s. 413-418. ISBN: 978-1-71386-230-7cs
dc.identifier.isbn978-80-88365-06-8-
dc.identifier.uri2-s2.0-85144113351&-
dc.identifier.urihttp://hdl.handle.net/11025/51038-
dc.description.abstractStředně manganové oceli patří do skupiny vysokopevných ocelí třetí generace, které vykazují vynikající kombinaci pevnosti a tažnosti. Jejich obsahem manganu se pohybuje okolo 3 až 12%. Po tváření za tepla je jejich struktura většinou tvořena martenzitickou matricí. Během interkritického žíhání dochází k reverzní přeměně martenzitu na austenit. Zvolení správného legování i parametrů interkritického žíhání, zejména teploty ohřevu, vede k získání dostatečně stabilního zbytkového austenitu, který výrazně ovlivňuje mechanické vlastnosti. Zbytkový austenit během deformace za studena vykazuje tzv. TRIP efekt a přispívá k výraznému deformačnímu zpevnění materiálu. Pro experiment byla zvolena středně manganová ocel s 0,2%C , 5% Mn a 3% Al, která byla po tváření za tepla podrobena různým režimům interkritického žíhání. Pro zvýšení stability zbytkového austenitu byla v oblasti bainitické přeměny provedena izotermická výdrž při různé teplotě. Pro ověření vlivu deformace byla odzkoušena i varianta s vloženou inkrementální deformací během ochlazování. Po zpracování byly získány martenzitické struktury s různým podílem bainitu, který byl podpořen výdrží na teplotě 425°C, feritem a zbytkovým austenitem. Mez pevnosti dosáhla až 1940 MPa s tažností okolo 10%.cs
dc.format6 s.cs
dc.format.mimetypeapplication/pdf-
dc.publisherTANGER Ltd.en
dc.relation.ispartofseriesProceedings 31st International Conference on Metallurgy and Materialsen
dc.rights© METALen
dc.subjectstředně manganová ocelcs
dc.subjecttepelné zpracovánícs
dc.subjecttermomechanické zpracovánícs
dc.subjectzbytkový austenitcs
dc.titleInfluence of processing parameters of medium manganese steel with 5% mn on the development of mechanical propertiesen
dc.title.alternativeVliv parametrů zpracování středně manganové oceli s 5% mn na vývoj mechanických vlastnostícs
dc.typekonferenční příspěvekcs
dc.typeConferenceObjecten
dc.rights.accessopenAccessen
dc.type.versionpublishedVersionen
dc.description.abstract-translatedMedium manganese steels belong to the group of third generation high-strength steels. These steels show an excellent combination of strength and ductility. Their manganese content is around 3 to 12%. After hot forming, their structure is mostly formed by a martensitic matrix. During intercritical annealing, martensite is reversed to austenite. The choice of the correct alloying and parameters of intercritical annealing, especially the heating temperature, leads to obtaining a sufficiently stable retained austenite, which significantly affects the mechanical properties. Retained austenite during cold deformation shows the so-called TRIP effect and contributes to significant deformation strengthening of the material. Medium manganese steel with 0.2% C, 5% Mn and 3% Al was chosen for the experiment and subjected to various intercritical annealing regimes after hot forming. To increase the stability of the retained austenite, isothermal hold at different temperatures was performed in the bainitic transformation region. To verify the effect of deformation, a variant with inserted incremental deformation during cooling was also tested. After processing, martensitic structures were obtained with varying portions of bainite, which was supported by the holding time at 425°C, ferrite and residual austenite. The yield strength reached up to 1940 MPa with an elongation of about 10%.en
dc.subject.translatedmedium manganese steelen
dc.subject.translatedheat treatmenten
dc.subject.translatedthermomechanical treatmenten
dc.subject.translatedretained austeniteen
dc.identifier.doi10.37904/metal.2022.4481-
dc.type.statusPeer-revieweden
dc.identifier.obd43937436-
dc.project.IDSGS-2022-012/Výzkum a vývoj moderních kovových materiálůcs
dc.project.IDIDEG-2021-026/Increasing the strength of permanent joints of additively produced and modern high-strength steelscs
dc.project.IDEF19_073/0016931/Zvyšování kvality interních grantových schémat na ZČUcs
Vyskytuje se v kolekcích:Konferenční příspěvky / Conference papers (KMM)
OBD

Soubory připojené k záznamu:
Soubor VelikostFormát 
metal2022_janda_metal (1).pdf822,98 kBAdobe PDFZobrazit/otevřít
Zobrazit minimální záznam Zobrazit statistiky


Použijte tento identifikátor k citaci nebo jako odkaz na tento záznam: http://hdl.handle.net/11025/51038

Všechny záznamy v DSpace jsou chráněny autorskými právy, všechna práva vyhrazena.

hledání
navigace
  1. DSpace at University of West Bohemia
  2. Publikační činnost / Publications
  3. OBD